pvc reinforce braided hose

CHARACTER:
1. Tenacity: After processing the polyester terylene by polymerization and intwining terylene in the mesosphere of the hose, the products are produced. So the cracking of products is very high.
2. Burliness: After affixing the PVC and Terylene by the special engineering technology, so there isn? the phenomena of abruption and stratification.
3. Permanence: The stuff which is choosed strictly and is processed with precise filter net under the consummate quality control system is made into products, wherefore the life-span is very lasting.
4. Pliability: The products are made by polymerizing terylene and mixing PVC for the best proportion, so the products are not only smooth but also soft.
AUTHENTICATION:
Our company have been authorized by ISO 9001:2000, on Nov. 22th, 2005.
ISO 9001:2000 Registered Date: 2005.11.22
ISO 9001:2000 Registered Number: 4809/0
QULITY
China Chemical Industry Standard Seoul? Own Back-check
Test Item Capability Test Condition Test Result
Test of Inner Pressure Bursting Pressure(Mpa) No leaking water, inflating and bursting 18.9Mpa below
no bursting 21.0Mpa
Coefficient of Curve Distortion ≥0.8 distortioncoefficient≥0.8 when curve radii is 145.44m 0.98
Stench Intensity Outer Tier ≥10.0Mpa 15.2
Endothecium ≥7.0 Mpa 29.1
Elongation Modulus Outer Tier ≥250% 300%
Endothecium ≥200% 305%
Agglutinate Intensity ≥1.5KN/m Speed of peeling 25.01 mm/min 2.6
WATCHFUL PROCEEDINGS:
1. The pressure is 60kgf/c㎡ below and the temperature is 70℃ below.
2. After using the products, they should be rolled. The place of safekeeping should be shady.
3. Must not knock the products by hammer when connecting hose, avoiding agglutinate disrepair